德固赛食品级PMMA ZK30     食品级PMMA 家用电器,卫生洁具应用

Plexiglas® Resist zk30聚甲基丙烯酸甲酯-丙烯酸Evonik Industries AG产品说明：

Product Profile:
PLEXIGLAS® Resist zk30 is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are:

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk30 is characterized by the following special properties:

good break resistance and impact strength

improved resistance to stress cracking

certified dishwasher resistance

AMECA listing.

Application:
Used for injection molding. Profile extrusion or coextrusion are also possible.

Examples:
lighting fixtures, writing and drawing utensils, domestic appliances and sanitaryware

Plexiglas® Resist zk30 物性表

基本信息

添加剂	冲击改性剂
特性	高 ESCR（抗应力开裂） 抗撞击性，高 清晰度，高 外观良好
用途	电器用具 家用货品 柔软的把手 卫浴产品 文具 型材
形式	粒子
加工方法	共挤出成型 挤出 注射成型
多点数据	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

物理性能额定值单位制测试方法

密度	1.15	g/cm³	ISO 1183
溶化体积流率（MVR） (230°C/3.8 kg)	1.40	cm³/10min	ISO 1133
吸水率 (平衡, 23°C, 50% RH)	0.34	%	ISO 62

机械性能额定值单位制测试方法

拉伸模量	2000	MPa	ISO 527-2/1
拉伸应力 (屈服)	51.0	MPa	ISO 527-2/50
拉伸应变 (屈服)	4.5	%	ISO 527-2/50
标称拉伸断裂应变	27	%	ISO 527-2

冲击性能额定值单位制测试方法

简支梁无缺口冲击强度 (23°C)	55	kJ/m²	ISO 179/1eU

热性能额定值单位制测试方法

热变形温度
0.45 MPa, 未退火	96.0	°C	ISO 75-2/B
1.8 MPa, 未退火	91.0	°C	ISO 75-2/A
玻璃转化温度	114	°C	ISO 11357-2
维卡软化温度	98.0	°C	ISO 306/B50
线形热膨胀系数 - 流动 (0 到 50°C)	1.1E-4	cm/cm/°C	ISO 11359-2

可燃性额定值
测试方法

UL 阻燃等级 (1.60 mm)	HB		UL 94

光学性能额定值单位制测试方法

折射率	1.490		ISO 489
透射率 1	90.0	%	ISO 13468-2

注射额定值单位制

干燥温度	< 88.0	°C
干燥时间	2.0 到 3.0	hr
加工（熔体）温度	230 到 240	°C
模具温度	50.0 到 70.0	°C

备注

1 .	D65